Synthesis of Mg$_2$IrH$_5$: A potential pathway to high-$T_c$ hydride superconductivity at ambient pressure

Abstract

Following long-standing predictions associated with hydrogen, high-temperature superconductivity has recently been observed in several hydride-based materials. Nevertheless, these high-$T_c$ phases only exist at extremely high pressures, and achieving high transition temperatures at ambient pressure remains a major challenge. Recent predictions of the complex hydride Mg$_{2}$IrH$_{6}$ may help overcome this challenge with calculations of high-$T_c$ superconductivity (65 K$~<~T_c~<~$ 170 K) in a material that is stable at atmospheric pressure. In this work, the synthesis of Mg$_{2}$IrH$_{6}$ was targeted over a broad range of $P$-$T$ conditions, and the resulting products were characterized using X-ray diffraction (XRD) and vibrational spectroscopy, in concert with first-principles calculations. The results indicate that the charge-balanced complex hydride Mg$_{2}$IrH$_{5}$ is more stable over all conditions tested up to ca 28 GPa. The resulting hydride is isostructural with the predicted superconducting Mg$_{2}$IrH$_{6}$ phase except for a single hydrogen vacancy, which shows a favorable replacement barrier upon insertion of hydrogen into the lattice. Bulk Mg$_{2}$IrH$_{5}$ is readily accessible at mild $P$-$T$ conditions and may thus represent a convenient platform to access superconducting Mg$_{2}$IrH$_{6}$ via non-equilibrium processing methods.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.