Phase diagram of pressure-induced high temperature superconductor La$_{3}$Ni$_{2}$O$_{7+δ}$

Abstract

We successfully synthesized samples of La$_{3}$Ni$_{2}$O$_{7+δ}$ ($δ= -0.50$, $-0.16$, $0.00$, $+0.01$, and $+0.12$) and measured the resistance under extremely high pressures using a diamond anvil cell to establish the electronic phase diagram. A Mott insulating state appears at $δ= -0.50$, where all Ni ions are divalent. With increasing oxygen content, superconductivity appears at $δ= 0.00$ and higher, above approximately 25 GPa, passing through Anderson localization at $δ= -0.16$. The superconducting transition temperature $T_{\mathrm{c}}$ decreases with increasing pressures for both $δ= 0.00$ and $+0.12$, with the pressure dependence of $T_{\mathrm{c}}$ being much stronger in the latter than in the former.