High-pressure self-flux growth and characterization of Li-deficient Li0.95FeAs single crystals

Abstract

Single crystals of LiFeAs were successfully grown by a self-flux method using the cubic anvil high-pressure and high-temperature technique. The reaction took place in a closed boron nitride crucible at a pressure of 1 GPa and a temperature of 1050 C. The grown crystals, retrieved from solidified lump, exhibit plate-like shapes with sizes up to 0.7 x 0.7 x 0.15 mm3. Single-crystal x-ray diffraction refinement confirmed the high structural perfection of the grown crystals (space group P4/nmm, No 129, Z = 2, a = 3.77370(10) A, c = 6.3468(6) A, and V = 90.384(9) A3) with the presence of a small deficiency on the Li site. The refined chemical composition of the produced crystals is Li0.95FeAs. Temperature-dependent magnetization measurements revealed bulk superconductivity with a superconducting transition Tc = 16 K. A comparative analysis of LiFeAs, Li1-xFeAs, and Li1-yFe1+yAs systems reveal that superconductivity is less sensitive to the Li deficiency, although it may completely disappear in the presence of both Fe excess and Li deficiency.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.