Enhancement of superconductivity on thin film of Sn under high pressure

Abstract

We investigated the pressure effects of a superconductivity on thin films of Sn. Elemental superconductor Sn with a body-centered tetragonal structure, $β$-Sn, exhibits superconductivity below the superconducting transition temperature ($T_{\rm c}=3.72$ K) at ambient pressure. $T_{\rm c}$ of Sn increases with lowering dimension such as in thin film and nanowire growth, or by high-pressure application. For thin films, $T_{\rm c}$ exhibits a slight increase up to approximately 4 K compared to the bulk value, attributable to the crystalline size and lattice disorder. By applying pressure on a bulk Sn, $T_{\rm c}$ initially decreases from 3.72 K as the pressure increases. Further increasing pressure up to 10 GPa, $T_{\rm c}$ increases to 5.3 K with the structural transformation. However, the combination of these effects on thin films of Sn, namely, thin-film growth and pressure effects, remains underexplored. In this study, we combined film-growth and pressure-application techniques to further increase $T_{\rm c}$ using a diamond anvil cell with boron-doped diamond electrodes. The drop of the electrical resistance suggesting the onset of $T_{\rm c}$ on the thin film reached above 6 K in $γ$-Sn phase. Further, the upper critical magnetic field was drastically enhanced. Atomic force microscopy suggests that the refinement of the grain size of the thin film under the non-hydrostatic pressure conditions contributes to stabilizing the higher $T_{\rm c}$ of $γ$-Sn.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.