Creation, stabilization, and study at ambient pressure of pressure-induced superconductivity in Bi$_{0.5}$Sb$_{1.5}$Te$_3$

Abstract

In light of breakthroughs in superconductivity under high pressure, and considering that record critical temperatures (T$_c$s) across various systems have been achieved under high pressure, the primary challenge for higher Tc should no longer solely be to increase T$_c$ under extreme conditions but also to reduce, or ideally eliminate, the need for applied pressure in retaining pressure-induced or -enhanced superconductivity. The topological semiconductor Bi$_{0.5}$Sb$_{1.5}$Te$_3$ (BST) was chosen to demonstrate our approach to addressing this challenge and exploring its intriguing physics. Under pressures up to ~ 50 GPa, three superconducting phases (BST-I, -II, and -III) were observed. A superconducting phase in BST-I appears at ~ 4 GPa, without a structural transition, suggesting the possible topological nature of this phase. Using the pressure-quench protocol (PQP) recently developed by us, we successfully retained this pressure-induced phase at ambient pressure and revealed the bulk nature of the state. Significantly, this demonstrates recovery of a pressure-quenched sample from a diamond anvil cell at room temperature with the pressure-induced phase retained at ambient pressure. Other superconducting phases were retained in BST-II and -III at ambient pressure and subjected to thermal and temporal stability testing. Superconductivity was also found in BST with T$_c$ up to 10.2 K, the record for this compound series. While PQP maintains superconducting phases in BST at ambient pressure, both depressurization and PQP enhance its T$_c$, possibly due to microstructures formed during these processes, offering an added avenue to raise T$_c$. These findings are supported by our density-functional theory calculations.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.