Overcoming Discharge Inhibition in n-Butane Oxidation: Two-Component BaTiO3 and Mn-Cu Mixed Oxide Coatings

Abstract

A twin surface dielectric barrier discharge on the microsecond scale was used in combination with a two-component coating to oxidize 300 ppm n-butane as a model volatile organic compound to CO2 and H2O in synthetic air at room temperature and at 160 °C. The integration of BaTiO3 as a base material for the coating allowed the successful use of otherwise discharge-ignition-inhibiting materials such as MnO2-CuO applied as a full coating. Application of pure BaTiO3 led to highly porous coatings that do not hinder the discharge ignition and show a negligible influence on n-butane conversion while reducing byproduct formation. Thus, BaTiO3 was identified as a suitable structure-directing agent in two-component coatings, using 1:1 and 1:2 ratios of BaTiO3:catalyst coatings. Coated electrode configurations were compared to their respective uncoated state to highlight the coating-induced changes. The two-component coatings strongly increased the CO2 selectivity, reaching a maximum of 91.6 % at an energy density of 450 J/L and 160 °C for the 1:2 ratio, corresponding to an increase of 51.0 % relative to the uncoated electrode.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.