Long-Term Stability of Superconducting Metal Superhydrides

Abstract

Zhou et al., in their recent publication (Nat. Commun. 16, 1135, 2025), reported the synthesis of lanthanum superhydride, LaHx (x = 10.2-11.1), by laser heating LaH3 with NH3BH3 at a pressure of 170 GPa and investigated the temporal evolution of the NMR spectra of the reaction products. They observed a gradual decrease in the 1H-NMR signal intensity assigned to the synthesized metal hydride, accompanied by an increase in molecular hydrogen within the sample chamber over a period of 50 days. Based on these observations, the authors concluded that LaH10 progressively decomposes into LaH3 and H2 within two months after synthesis at its formation pressure of 170 GPa. Here, we demonstrate that, under their formation conditions, metal superhydrides are thermodynamically more stable than metal trihydrides. Furthermore, we present direct experimental evidence - based on X-ray diffraction and four-probe electrical resistance measurements - confirming the stability of both the crystal lattice and high-temperature superconducting properties of the Fm-3m-LaH10 phase for more than five years. This long-term stability is consistent with predictions from quantum chemistry calculations.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.