X-ray Diffraction and Electrical Transport Imaging of Superconducting Superhydride (La,Y)H10

Abstract

We report the synthesis and characterization of (La0.9Y0.1)H10 superhydrides exhibiting coexisting cubic Fm-3m and hexagonal P63/mmc clathrate phases observed over the pressure range from 168 GPa down to 136 GPa. Using synchrotron-based X-ray diffraction imaging (XDI) at the upgraded Advanced Photon Source (APS-U), we spatially resolved micron-scale distributions of these phases, revealing structural inhomogeneity across the sample. Four-probe DC resistance measurements confirmed superconductivity, with two distinct transitions: an onset at 244 K associated with the cubic phase and a second near 220 K linked to the hexagonal phase. Notably, resistance profiles collected from different current and voltage permutations showed variations in transition width and onset temperature that correlated with the spatial phase distribution mapped by XDI. These findings demonstrate a direct connection between local structural domains and superconducting behavior. Yttrium substitution is found to influence both the phase behavior and superconducting properties of LaH10-type clathrate hydrides. More broadly, this study highlights the utility of spatially correlating structural and electrical transport measurements in materials exhibiting heterogeneity under pressure, including hydride superconductors.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.