Same-group element replacement enhances superconductivity in clathrate-like YH4

Abstract

H3S, LaH10, and hydrogen-based compounds have garnered significant interest due to their high-temperature superconducting properties. However, the requirement for extremely high pressures limits their practical applications. In this study, YH4 is adopted as a base material, with partial substitution of Yttrium (Y) by Scandium (Sc), Lanthanum (La), and Zirconium (Zr). Pure YH4, stable at 120 GPa, exhibits a critical temperature (Tc) of 84-95 K. Substituting half of the Y atoms increases Tc to 124.43 K for (Y,Sc)H4 at 100 GPa but reduces it to 101.24 K for (Y,La)H4 at 120 GPa. In contrast, (Y,Zr)H4 at 200 GPa shows a further suppressed Tc of 69.55 K. The remarkable superconductivity in (Y,Sc)H4 might be related to its unique phonon dispersion without optical-acoustic gap, compressed Y-H bonds, and significant electron delocalization under pressure, collectively boosting electron-phonon interactions. Furthermore, the lowest optical phonons play a crucial role in the superconductivity of these materials. This work suggests that substituting Y with same-group metal elements is an effective strategy to enhance Tc in hydride superconductors.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.