Non-Fermi liquid behavior in La$_3$Ni$_2$O$_7$ thin films under hydrostatic pressure

Abstract

The discovery of superconductivity in bilayer nickel-oxides has revived an intense effort to understand the potential of high-temperature superconductivity in these materials and their relation to cuprate superconductors. In this work, we investigate the growth and properties of bilayer La$_3$Ni$_2$O$_7$ thin films as a function of substrate, oxygen treatment and applied pressure in order to study the evolution of transport properties. We report epitaxial growth of La$_3$Ni$_2$O$_7$ thin films on LaAlO$_3$ (LAO) (001) and SrLaAlO$_4$ (SLAO) (001) substrates, and the effects of ex-situ annealing in a high pressure furnace under an oxygen-rich environment. Transport measurements show that the La$_3$Ni$_2$O$_7$ thin films on LAO(001) exhibit Fermi liquid-like metallic behavior with a slight Kondo-like upturn at low temperatures, which evolves with the application of modest hydrostatic pressures toward non-Fermi liquid behavior with a temperature dependence of resistance approaching $\sim$ T$^{1.4}$ at 1.41 GPa. The ability to tune the normal state resistivity of La$_3$Ni$_2$O$_7$ films to display non-Fermi liquid behavior under such a modest hydrostatic pressure range - only 6 - 8 % of that typically applied via diamond anvil cell (DAC) in La$_3$Ni$_2$O$_7$ single crystals to achieve comparable effects - is both noteworthy and unexpected. These findings imply the strong tunability of La$_3$Ni$_2$O$_7$ in thin film form and the likely proximity of a strongly fluctuating ordered state leading to non-Fermi liquid behavior under even modest applied pressures.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.