Superconductivity in the high-pressure tetragonal phase of UTe2

Abstract

Electrical transport and magnetic measurements have been made on UTe2 under pressure P up to approximately 16 GPa to determine the superconducting transition temperature Tc vs P phase diagram in the high-pressure tetragonal phase. Superconductivity emerges near 5 GPa, coincident with the orthorhombic to tetragonal phase transition; in the tetragonal phase, Tc reaches a maximum value of approximately 4 K at 6 GPa and then decreases with P and appears to vanish near 18 GPa. Tetragonal UTe2 has a relatively small upper critical field Hc2(0) $\approx$ 1.2 T at 5.3 GPa, smaller than the Pauli paramagnetic limit, and is orbitally limited with a coherence length $ξ$tetra $\approx$ 16.5 nm. This small value of Hc2(0) favors more conventional superconductivity; in contrast, the large values of Hc2(T) for orthorhombic UTe2 exceed the Pauli paramagnetic limit in all three crystallographic directions and have been attributed to unconventional superconductivity, widely believed to involve spin-triplet pairing. The temperature-pressure phase diagram of UTe2 shows a striking dichotomy: a narrow, fragile, unconventional superconducting region in the orthorhombic phase vs a broad, robust, and more conventional superconducting dome in the tetragonal phase. This dichotomy is consistent with the proposal that U-dimers, present (absent) in the orthorhombic (tetragonal) phase, may play a role in spin-triplet superconductivity of orthorhombic UTe2. In the tetragonal phase, the normal-state electrical resistivity $ρ$(T) exhibits metallic behavior with a knee between 200 and 240 K that depends weakly on P and most likely marks the onset of a transition to a magnetically ordered phase that coexists with superconductivity.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.