Terahertz Time-Domain Spectroscopy as a Universal Defect Fingerprinting Tool for Organic Halide Perovskite Solar Cells

Abstract

Organic-inorganic hybrid perovskites (OHPs) deliver certified single-junction power conversion efficiencies (PCEs) exceeding 26% and perovskite-silicon tandem values surpassing 34%, yet a substantial gap with the Shockley-Queisser (S-Q) limit persists-primarily due to grain-boundary (GB) defects that drive non-radiative recombination, ion migration, and degradation. Rational passivation demands a non-contact tool capable of identifying and quantifying specific defect species in device-relevant thin films, a capability absent from conventional probes. This short review demonstrates that terahertz time-domain spectroscopy (THz-TDS, 0.3-3.0 THz) fulfills this role. Across four OHP compositions fabricated by sequential vacuum evaporation (SVE)-MAPbI3, MAPbBr3, FAPbI3, and CsPbI3-the THz spectral window captures both intrinsic phonon modes and GB-localized molecular defect vibrations, enabling species-specific, quantitative characterization at room temperature. Notably, the oscillator strength of the SVE-specific 1.58 THz absorption in MAPbI3 scales linearly with XPS-quantified CH3NH2 defect concentration, establishing THz-TDS as a direct, non-destructive defect meter. Building on these findings, we propose a three-pillar framework for THz-guided defect engineering: (I) quantitative defect measurement via oscillator-strength analysis, (II) material-specific fingerprint identification from a systematically constructed THz library, and (III) fingerprint-guided defect elimination with real-time feedback-together defining a closed-loop quality-control cycle that connects spectroscopic diagnosis to passivation strategy and, ultimately, to enhanced solar-cell efficiency.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.