Numerical exploration on unveiling the photovoltaic potential of MgXS3(X = Ti, Zr, Hf) chalcogenide perovskites

Abstract

Lead-free chalcogenide perovskites offer a nontoxic and thermally robust path beyond Pb-based perovskite solar cells (PSCs), but their device-level behavior in realistic three-dimensional geometries remains insufficiently characterized. In this work, we investigate ZnSe/MgXS3(X = Ti, Zr, Hf)/Sb2S3 solar cell architecture where MgXS3 absorbers from the II-IV-VI chalcogenide perovskite family is employed as the absorber layer. The device is analyzed using 3D finite-element simulations in COMSOL Multiphysics that self-consistently couple optical generation, drift-diffusion carrier transport, and heat transfer under AM 1.5G 1-sun illumination, following a fully coupled opto-electro-thermal framework. For each absorber composition, the impacts of absorber thickness, doping, and defect density are systematically investigated, and the contribution of an Sb2S3 back-surface-field (BSF) layer to carrier collection and spectral response is quantified. Under optimized conditions, MgZrS3, MgTiS3, MgHfS3-based devices achieves a simulated power conversion efficiency (PCE) of 28.18%, 26.72%, and 28.16%, respectively. The corresponding open-circuit voltage (VOC) values are 0.94 V, 0.74 V, and, 1.07 V while the short-circuit current density (JSC) values are 34.46 mA/cm2, 42.69 mA/cm2, and 29.89 mA/cm2, with fill factor (FF) values of 86.99%, 84.58%, and 88.02%, respectively. Coupled electro-thermal simulations further reveal a small spatially non-uniform steady-state temperature rise across the ultrathin cell stack, mainly governed by non-radiative recombination and Joule dissipation within the active layers. Overall, these results confirm MgXS3(X = Ti, Zr, Hf) chalcogenide perovskites as promising lead-free absorber materials and offer practical design guidance for achieving high-efficiency, thermally stable three-dimensional device architectures.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.