Wrinkles and Magnetic Flux Trapping in Graphite Nanoflakes: A Possible Source and Manifestation of Room-Temperature Superconductivity

Abstract

The paper reports on a possible manifestation of local high-temperature superconductivity in graphite nanoflakes obtained from the bulk pyrolytic graphite by an extended grinding and subsequent annealing at 670 K in the air. Analysis of transmission electron microscopy (TEM) images shows that such treatment leads to a formation of high-density wrinkle-type defects at the basal-plane surface. The sample reveals the magnetic flux trapping - one of the key signatures of superconductivity - that persists up to 390 K and above. At the same time, both the as-ground (unannealed) and annealed in the vacuum samples manifest negligible flux trapping, and no wrinkles in their TEM images were found. The direct correlation between the appearance of high-density wrinkle arrays and the detection of the trapped magnetic flux above the room temperature strongly suggests that wrinkled regions serve a source of local high-temperature superconductivity in graphite.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.