Divergent Solid-state Conversion Pathways in Evaporated All-perovskite Tandem Solar Cells

Abstract

Sequential thermal evaporation (sTE) is emerging as a solvent-free route to high-quality mid-bandgap perovskites, but its extension to mixed-halide wide-bandgap (WBG) and Sn-Pb narrow-bandgap (NBG) absorbers for all-perovskite tandem solar cells (TSCs) remains limited by an incomplete understanding of solid-state conversion. Here, using time-sliced ex situ analysis, we reveal divergent solid-state conversion mechanisms in sequentially evaporated WBG and NBG precursor stacks. In WBG stacks, formamidinium (FA)-containing species penetrate the inorganic template and Br/I redistribution precedes substantial three-dimensional perovskite formation. The photoactive phase then crystallizes from a chemically mixed reservoir, and absolute PbBr$_2$ thickness, rather than nominal PbBr$_2$/PbI$_2$ ratio, determines the final bandgap. In NBG stacks, by contrast, an early Pb-rich perovskite phase forms upon formamidinium iodide deposition, restricting further FA penetration into the buried SnI$_2$ precursor. Subsequent annealing promotes rapid lattice reorganization faster than Sn/Pb interdiffusion, leaving vertical compositional gradients. Guided by these insights, we develop sTE absorbers with bandgaps spanning 1.26-1.96 eV and demonstrate the first evaporated all-perovskite TSC, reaching a power conversion efficiency of 19.2%. Encapsulated tandems retain on average 80% of their initial efficiency after 1,200 h at 65 $^\circ$C (ISOS-D-2). These results establish bandgap-specific control of solid-state conversion as a design principle for sequentially evaporated perovskite tandem photovoltaics.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.