Tunneling Spectroscopy Study of Low Baked Bulk Niobium for Superconducting RF Cavity Applications

Abstract

Point-contact tunneling (PCT) spectroscopy was used to probe the local superconducting properties of cavity-grade niobium following surface treatments representative of superconducting radio-frequency (SRF) cavities. Electropolished (EP) samples were compared with samples baked at 120~$^\circ$C for 48 h and subjected to a two-step bake at 75~$^\circ$C for 2 h followed by 120~$^\circ$C for 48 h. Although the superconducting gap $Δ$ is predominantly distributed around the bulk Nb value (~1.5 meV), regions exhibiting strongly suppressed gaps (minigaps) are observed in 15--29% of junctions on EP samples. Their occurrence decreases to 6% after the 120~$^\circ$C bake and to only 1% after the two-step treatment. Spectra exhibiting minigaps are well described by the Usadel proximity-effect model, consistent with superconducting Nb coupled to normal regions that we attribute to hydride formation. These results provide direct microscopic evidence that low-temperature baking suppresses regions of degraded surface superconductivity in cavity-grade Nb. The pronounced reduction achieved by the two-step bake further supports a link between hydride-related proximity effects and the surface superconducting properties governing SRF cavity performance.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.