Abstract
We investigate the impact of a monolithic three-dimensional (M3D) integration process-critical $400^\circ$C post-processing forming gas anneal (FGA) on the electrical performance, reliability, and defect evolution of oxide-channel thin-film transistors (TFTs), combining systematic experiments with density-functional-theory (DFT)-based liquid-quench molecular-dynamics (MD) simulations. Indium tungsten oxide (IWO) TFTs are employed as a model system and encapsulated with a thin 3 nm Al$_2$O$_3$ / 3 nm HfO$_2$ hybrid layer that effectively suppresses external hydrogen ingress. We reveal a non-monotonic evolution of device behavior during FGA, governed by initial densification followed by partial crystallization. Short-duration FGA (10 min) induces channel densification and the formation of shallow, delocalized defect states, leading to pronounced positive bias temperature instability (PBTI) degradation and the emergence of a characteristic transfer-curve "kink." With prolonged annealing (>40 min), partial crystallization of the oxide channel occurs, stabilizing hydrogen in deep, localized defect states, suppressing hydrogen mobility, and restoring device reliability. As a result, the PBTI shift is reduced to 10.4 mV after 2000 seconds of stress, accompanied by complete elimination of the transfer-curve kink. These findings provide a mechanistic understanding of hydrogen-defect interactions during high-temperature post-processing FGA and demonstrate that appropriate hydrogen-blocking encapsulation enables oxide-channel TFT integration without compromising electrical performance or reliability.
Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.
Record
- Archive ID
- arxiv:2609.22509
- Published
- Sep 18, 2026
- Venue
- IEEE Transactions on Electron Devices, vol. 73, no. 5, pp. 3140-3148 (2026)
- DOI
- 10.1109/ted.2026.3658060
- arXiv
- 2609.22509
- Categories
- cond-mat.mtrl-sci, physics.app-ph
- Provenance
- arxiv