Distinguishing sodium-ion penetration and sustained transport in realistic hard carbon nanostructures

Abstract

Hard carbons are promising anodes for sodium-ion energy storage, yet the relationship between their heterogeneous microstructure and sodium transport remains poorly understood. Here, we combine machine-learning-generated hard-carbon structures with molecular dynamics simulations of explicit 1 M NaPF6 in ethylene carbonate/dimethyl carbonate electrolyte to investigate sodium storage and transport across carbon structures with densities from 0.5 to 2.0 g cm-3. Increasing carbon density produces less accessible pore networks and greater graphitic local ordering, allowing the influence of microstructure on electrochemical response and Na+ transport to be examined systematically. Sodium uptake increases with applied potential but decreases strongly with carbon density, while electrode charging persists even in the densest structure, where Na+ uptake remains very small. Coordination analysis shows increasing interaction with the carbon framework under applied potential, while Na+ retains a partially solvated environment. Three-dimensional trajectory analysis reveals heterogeneous, predominantly tortuous transport pathways, with the more open HC-C1 structure supporting broader penetration and greater sustained displacement. Maximum penetration depth and retained displacement are not equivalent: ions can transiently reach deep regions of denser carbon structures before returning towards the electrolyte interface. Potential-of-mean-force analysis further shows that deep penetration occurs across a range of projected free-energy changes and cannot be described by a single energetic criterion. These results show that Na+ storage and transport are governed by the interplay between electrostatic driving force, electrolyte solvation, pore accessibility and confinement, highlighting carbon microstructure as a key determinant of sustained ionic penetration.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.