Delamination in Large REBCO Coils

Abstract

REBCO coated conductors have been used in ultrahigh field magnets for condensed matter physics research, nuclear fusion, particle accelerators, and NMR applications. It is well known, however, that they are not mechanically strong against delamination due to their intrinsic layered structures. As a result, the delamination issue has become one of the major design challenges of REBCO magnet coils. As a part of the development of the 40 T all-superconducting magnet at the National High Magnetic Field Laboratory, USA, large-scale coils wound by two-in-hand REBCO conductor with turn-to-turn insulation was designed and tested at 4.2 K in an 11.4 T background magnetic field. We found REBCO degradations within the windings and at the crossover joints during the tests. The postmortem inspection found that the degradation was caused by delamination. The delamination appears on the surface of the conductor as bubbles which were subsequently studied by microscopy. Additionally, a similar bubble was found on a short sample by torque magnetometry. This supports the inference that the delamination bubbles found in coils are due to electromagnetic stress. In this paper, we present these findings. The implication of these findings for future magnet designs and the method of mitigation will be discussed.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.