Pressure-induced double-dome superconductivity in doped kagome metal Cs(V0.86Ta0.14)3Sb5 without charge density wave

Abstract

The vanadium-based kagome superconductor CsV$_3$Sb$_5$ exhibits an intricate interplay between charge density wave (CDW) and superconductivity (SC). Substituting Ta for V will suppress the CDW order and enhance superconductivity. Here, we report a high-pressure study up to 48 GPa on Ta-doped Cs(V$_{0.86}$Ta$_{0.14}$)$_3$Sb$_5$ with enhanced $T_\mathrm{c}$ around 5.29 K and without CDW order. At low pressures, unlike the characteristic $``$M-shaped" temperature-pressure phase diagram of the pristine CsV$_3$Sb$_5$, the Ta-doped compound exhibits a distinct non-monotonic evolution. Initially, $T_\mathrm{c}$ drops slightly from 5.29 K at ambient pressure to 4.90 K at 0.33 GPa, before increasing to a maximum of 5.70 K at 0.61 GPa. Upon further compression, $T_\mathrm{c}$ decreases continuously to 0.98 K at 12.3 GPa. At higher pressures, $T_\mathrm{c}$ rises again, reaching 4.46 K at 47.7 GPa. This evolution of $T_\mathrm{c}$ establishes two superconducting domes under pressure, which are similar to those in CsV$_3$Sb$_5$. Our results demonstrate that pressure-induced double-dome superconductivity is intrinsic to these V-based kagome superconductors, even in the absence of long-range CDW order.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.