Synergistic Graphene and PEDOT:PSS Layers on Silicon for Enhanced Efficiency and Stability in Schottky Junction Solar Cells

Abstract

While graphene/n-type silicon (Gr/n-Si) and PEDOT:PSS/n-Si solar cells offer a cost-effective alternative to conventional photovoltaics, achieving simultaneous high power conversion efficiency (PCE) and long-term environmental stability remains a formidable challenge. Here, we report the synergistic enhancement of both performance and stability in a planar trilayer PEDOT:PSS/Gr/n-Si Schottky junction architecture. By systematically benchmarking this hybrid device against pristine Gr/n-Si and PEDOT:PSS/n-Si reference cells fabricated on untextured substrates, we isolate the fundamental optoelectronic and barrier functions of the carbon lattice. Comprehensive analyses reveal that the PEDOT:PSS layer simultaneously functions as an anti-reflection coating, a moderate p-type dopant for the underlying graphene, and a conductivity enhancer, collectively optimizing interfacial charge transport. Consequently, the trilayer device achieves a PCE of 8.52%, markedly outperforming the pristine Gr/n-Si reference cell (4.56%). Crucially, the atomic impermeability of the graphene sheet serves as a robust environmental barrier. While bare PEDOT:PSS/n-Si junctions retained only ~29% of their initial efficiency after 75 days of ambient exposure, graphene shields the active junction from moisture-induced degradation of the hygroscopic PEDOT:PSS overlayer. This enables the trilayer device to retain approximately 90% of its initial efficiency over the same 75-day period. The complementary roles of graphene as both a highly crystalline charge transport interface and an impermeable protective barrier establish a highly effective strategy for engineering high-efficiency, environmentally stable hybrid photovoltaics.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.