Emergent altermagnetism in (LaVO$_3$)$_n$/(LaNiO$_3$)$_m$ superlattices from interfacial charge transfer and octahedral tilts

Abstract

Using first-principles calculations, we show that altermagnetism emerges in (LaVO$_3$)$_n$/(LaNiO$_3$)$_m$ superlattices, with $(n,m) = (1,1), (2,2)$ and $(2,4)$, from the interplay of interfacial charge transfer and octahedral tilts. Charge transfer drives the system towards the V$^{4+}$ and Ni$^{2+}$ configuration, turning the otherwise paramagnetic nickelate layers into a magnetically active sublattice. The resulting $C$-type antiferromagnetic order, combined with $a^-b^+c^-$ or $a^-b^-c^-$ octahedral tilts, links opposite-spin sublattices only through nonsymmorphic operations, yielding a $d$-wave spin splitting without spin-orbit coupling. Within DFT+U, the splitting reaches 118 meV in the insulating (LVO)$_1$/(LNO)$_1$ superlattice, about twice that calculated for bulk LaVO$_3$, and decreases as the nickelate layers become thicker. Our findings indicate that this splitting is hosted by both the V and Ni sublattices, with nearly half of its weight on oxygen $2p$ states through $p$-$d$ covalency. Interfacial charge transfer thus emerges as a \textit{design} principle for engineering altermagnetism in oxide heterostructures.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.