Decoding Composition-Structure-Performance Relations in Sodium Layered Oxide Positive Electrode Materials

Abstract

Layered sodium transition-metal (TM) oxides, Na$_x$TMO$_2$, are among the most promising sodium-ion positive electrode materials, yet their Na/vacancy orderings, layer stacking sequences, and cooperative Jahn--Teller distortions are known only for a few single-TM compounds. We compile the Na/vacancy orderings reported in earlier studies into a single library of 41 unique orderings and apply this uniformly to five single-TM and all ten Na$_x$TM$_{0.5}$TM$'_{0.5}$O$_2$ oxides (TM = Ti, Mn, Fe, Co, Ni), screening more than 120,000 structures with machine-learning interatomic potentials prior to 1,025 accurate first-principles calculations. The phase diagrams explain the observed O3/P3/O1 sequences and voltages, and the O3-to-P3 competition hinges on ordering energies of a few meV per atom that scalar descriptors, such as the cationic potential and the interlayer-slab distance, miss. Our extensive analysis reveals that the redox couples form a nearly partner-independent ladder, Ti$^{3+/4+}$ $<$ Mn$^{3+/4+}$ $<$ Co$^{3+/4+}$ $<$ Ni$^{2+/3+}$ $<$ Fe$^{3+/4+}$, explaining pristine charge transfer and the oxidation sequence. Van Vleck analysis of every TMO$_6$ octahedron reveals that TM mixing suppresses the cooperative Jahn--Teller distortions of Mn$^{3+}$ and Ni$^{3+}$ through charge transfer to Jahn--Teller-inactive states or dilution of Jahn--Teller-active centers. We formulate an energy-density-versus-strain map that yields a design rule: a high-voltage couple without Jahn--Teller strain, which Mn$^{4+}$/Ni$^{2+}$ charge transfer realizes in Na$_x$Mn$_{0.5}$Ni$_{0.5}$O$_2$, the most practical composition. We release the ordering-resolved dataset as a training set for subsequent training of accurate machine-learning interatomic potentials.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.