Computational screening of amorphous lithium trivalent-metal chloride solid-state electrolytes

Abstract

Amorphous solid-state electrolytes (SSEs) are attractive candidates for safe, high-energy-density all-solid-state batteries. The recent discovery that amorphous LiTaCl$_6$ and LiNbCl$_6$ reach room-temperature ionic conductivities above 10 mS cm$^{-1}$ with activation energies below 0.2 eV has spurred a broad search for new amorphous halide Li conductors. Here we report a computational screening of amorphous lithium trivalent-metal chlorides (Li-M(III)-Cl) using molecular dynamics driven by a universal machine-learning force field. For the sixteen Li-M(III)-Cl compositions spanning fifteen rare-earth elements and indium, all phases exhibit fast room-temperature Li$^+$ diffusion, with diffusivities of roughly $2$-$5 \times 10^{-7}$ cm$^2$ s$^{-1}$. After scaling the conductivity versus diffusivity relation to an experimental LiTaCl$_6$ reference, the estimated room-temperature conductivities range from 7.7 mS cm$^{-1}$ for amorphous Li$_3$InCl$_6$ to 14 mS cm$^{-1}$ for amorphous Li$_3$ScCl$_6$. With a low activation energy of 0.18 eV, amorphous Li$_3$ScCl$_6$ is predicted to be among the most conductive amorphous halide electrolytes. To rationalize the composition-dependent transport, we identify two descriptors: the Li$^+$ vibrational density of states (VDOS) center, which correlates inversely with diffusivity, and the average number of correlated bodies in string-like Li$^+$ motion. Compositions in which Li$^+$ has a lower VDOS center and migrates more by individual hopping rather than by concerted motion exhibit higher Li-ion diffusivities. These results suggest rich Li-ion transport characteristics in amorphous halide SSEs.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.