Prussian blue and Prussian white thin-film electrodes: Single-step electrodeposition for anode and cathode applications

Abstract

This study examines how deposition potential influences the composition and nanoscale structure of Prussian Blue (PB)/Prussian White (PW)-family films, providing an experimental basis for assessing their proposed functions. Films were grown directly on Au/Cr/Si in a single potentiostatic step from a common aqueous bath at $-0.20$ to $+0.40$\,V versus a saturated calomel electrode, with a fixed deposition charge of 10\,mC. Electron microscopy, elemental analysis, X-ray photoelectron spectroscopy, and Raman spectroscopy revealed potential-dependent chemistry and nonmonotonic morphology. EDS indicated greater K incorporation in lower-potential deposits, whose Fe~2p and Raman features were consistent with more reduced, PW-like environments. Surface K/Fe ratios varied nonmonotonically from 1.129 to 1.322 across the series, corresponding to 52.95--56.94\% K within the detected K+Fe population. Larger faceted crystallites at $+0.30$\,V contrasted with finer pyramids and cracks at $+0.40$\,V. Selected PB-like and PW-like regions had local cubic lattice parameters of $(10.31\pm0.10)$\,Å and $(10.36\pm0.10)$\,Å, respectively; their overlapping uncertainties prevent discrimination by lattice spacing alone. Cross-sectional maps showed broadly uniform framework-element distributions within locally continuous coatings. Together, these observations relate deposition conditions to contrasting chemical and morphological starting states without establishing bulk stoichiometry or phase purity. A literature-grounded outlook identifies ion storage, sensing, electrochromism, resistive switching, and ion handling as research opportunities requiring functional validation in these films.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.