Amorphous selenium-alloyed TeOx thin-film solar cells

Abstract

Tellurium dioxide (TeO$_2$) is a wide-bandgap oxide with attractive processing versatility and emerging p-type semiconducting behaviour, making it a promising material system for optoelectronic and photovoltaic applications. However, TeO$_2$-derived thin films prepared by scalable manufacturing processes, such as vacuum sublimation, can contain residual metallic Te$^0$ species that introduce trap states, limit hole transport, and promote carrier recombination. Here, we demonstrate a selenium alloying strategy to control the defect chemistry of vacuum-sublimed TeO$_x$ films. TeO$_2$:Se powder mixtures (90:10~wt\%) were thermally evaporated and subsequently annealed in air at 225~$^\circ$C for up to 9~h, yielding amorphous TeO$_x$:Se films with an optical bandgap of 0.98~eV under optimised conditions. Structural, chemical, optical, and electrical analyses show that prolonged annealing promotes Se redistribution, suppresses residual Te$^0$ to approximately 0.4\%, reduces the film's surface roughness, and shifts the valence-band edge. To evaluate the potential of TeO$_x$:Se for photovoltaic applications, we fabricated thin-film solar cells with an ITO/ZnO/TeO$_x$:Se/MoO$_x$/Ag architecture. Devices based on an 80~nm TeO$_x$:Se active layer annealed for 9~h exhibit optimal performance, with broadband photocurrent generation from 300 to 1000~nm, yielding an open-circuit voltage of 0.50~V, a short-circuit current density of 8.50~mA~cm$^{-2}$, a fill factor of 0.44, and a maximum power conversion efficiency of approximately 1.87\%. These results establish selenium-alloyed TeO$_x$ as a viable oxide-derived absorber for thin-film photovoltaics and highlight chemical-state control as an effective route for improving photovoltaic performance.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.