High Pressure Studies of Tc and Lattice Parameters of MgB2

Abstract

We performed ac-susceptibility measurements of magnesium diboride powder samples under pure hydrostatic pressures up to 0.4 GPa and under quasi-hydrostatic pressure conditions up to 8 GPa in a helium gas pressure cell and a diamond-anvil cell (DAC), respectively. Furthermore, the DAC has been used to investigate the lattice compression by X-ray diffraction. Under helium gas pressure the superconducting transition temperature shows a linear decrease dTc/dp = -1.13 K/GPa. The pressure effect is fully reversible with a return to the initial Tc of 37.5 K after pressure release. In the diamond-anvil cell the application of pressure leads to a stronger Tc-decrease than in the helium gas pressure cell, and after the release of pressure a degradation effect with lower Tc and a broader transition compared to the first measurement at ambient pressure occurs. Such degradation may be explained by shear stresses and uniaxial pressure components, which cannot be avoided in a DAC at low temperatures. Considering the anisotropic AlB2-type structure with alternating honeycomb boron and magnesium layers, MgB2 seems to be very sensitive to such non-hydrostatic pressure components, which would explain the spread of dTc/dp values reported in the literature.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.