A ferroelectric semiconductor field-effect transistor

Abstract

Ferroelectric field-effect transistors employ a ferroelectric material as a gate insulator, the polarization state of which can be detected using the channel conductance of the device. As a result, the devices are of potential to use in non-volatile memory technology, but suffer from short retention times, which limits their wider application. Here we report a ferroelectric semiconductor field-effect transistor in which a two-dimensional ferroelectric semiconductor, indium selenide (α-In2Se3), is used as the channel material in the device. α-In2Se3 was chosen due to its appropriate bandgap, room temperature ferroelectricity, ability to maintain ferroelectricity down to a few atomic layers, and potential for large-area growth. A passivation method based on the atomic-layer deposition of aluminum oxide (Al2O3) was developed to protect and enhance the performance of the transistors. With 15-nm-thick hafnium oxide (HfO2) as a scaled gate dielectric, the resulting devices offer high performance with a large memory window, a high on/off ratio of over 108, a maximum on-current of 862 μA μm-1, and a low supply voltage.

Abstract: arXiv descriptive metadata (CC0). Thank you to arXiv for use of its open access interoperability. This service was not reviewed or approved by, nor does it necessarily express or reflect the policies or opinions of, arXiv.